Kakaretso
OBC-35S ke tlatsetso ea tahlehelo ea mokelikeli oa polymer bakeng sa samente e sebelisoang selibeng sa oli mme e entsoe ka copolymerization e nang le AMPS e le monoma e kholo e nang le mocheso o motle le ho hanyetsa letsoai le ho kopantsoe le li-monomers tse ling tse khahlanong le letsoai.Limolek'hule li na le palo e kholo ea lihlopha tse khahlang haholo tse kang - CONH2, - SO3H, - COOH, e phethang karolo ea bohlokoa ho hanyetsa letsoai, ho hanyetsa mocheso, ho monya metsi a mahala, ho fokotsa tahlehelo ea metsi, joalo-joalo.
OBC-35S e na le mekhoa e metle ea ho feto-fetoha ha maemo 'me e ka sebelisoa mefuteng e fapaneng ea litsamaiso tsa seretse sa samente.E na le tumellano e ntle le li-additives tse ling 'me e phetha karolo ea ho khothalletsa viscosity le ho emisa ka lebaka la boima bo boholo ba limolek'hule.
OBC-35S e loketse mocheso o pharaletseng o hanyetsanang le mocheso o phahameng ho fihlela ho 180 ℃.Ka mor'a ho sebelisoa, metsi a tsamaiso ea samente ea slurry e ntle, e tsitsitse ka mokelikeli o sa lefelloeng 'me ntle le ho lieha ho beha le matla a hōla kapele.
OBC-35S e loketse ho kopanya metsi a hloekileng / letsoai la metsi a letsoai.
Lintlha tsa tekheniki
| Ntho | Index |
| Ponahalo | Phofo e tšoeu |
Ts'ebetso ea slurry ea samente
| Ntho | Tindex ea boenjiniere | Boemo ba teko |
| Ho lahleheloa ke metsi, ml | ≤100 | 80℃,6.9MPa |
| Nako e teteaneng, min | ≥60 | 80℃,45MPa/45min |
| Ho tsitsa ha pele, Bc | ≤30 | |
| Matla a hatellang, MPa | ≥14 | 80 ℃, khatello e tloaelehileng, 24h |
| Metsi a mahala, mL | ≤1.0 | 80 ℃, khatello e tloaelehileng |
| Sebopeho sa slurry sa samente: 100% samente ea sehlopha sa G (ho hanyetsa sebabole se phahameng) + 44.0% metsi a hloekileng + 0.7% OBC-35S + 0.5% defoamer. | ||
Sebaka sa tšebeliso
Mocheso: ≤180 ° C (BHCT).
Tlhahiso ea litekanyetso: 0.6% -3.0% (BWOC).
Sephutheloana
OBC-35S e pakiloe ka mokotleng oa lik'hilograma tse 25 ho tse tharo ho e le 'ngoe, kapa e pakiloe ho latela litlhoko tsa bareki.
Ela hloko
OBC-35S e ka fana ka lihlahisoa tsa metsi OBC-35L.