ʻO ka OBC-43S kahi mea hoʻohui wai hoʻoheheʻe wai ʻaila polymer.He copolymerized me AMPS / NN, he kū'ē maikaʻi i ka mahana a me ka paʻakai, e like me ka monomer nui, i hui pū me nā monomers paʻakai.Hoʻokomo ka huahana i nā pūʻulu ʻaʻole maʻalahi i ka hydrolyzed, ʻike ʻia ka hoʻonui ʻia ʻana o ke kūpaʻa wela kiʻekiʻe, a loaʻa i ka mole ka nui o nā pūʻulu adsorption ikaika e like me -CONH2, -SO3H, -COOH, kahi mea nui i ka pale ʻana i ka mahana, adsorption. o ka wai manuahi, a me ka lilo o ka wai.
OBC-43S he versatility maikaʻi, hiki ke hoʻohana ʻia i nā ʻano ʻōnaehana slurry sima, a loaʻa maikaʻi ke kūlike me nā mea hoʻohui ʻē aʻe.
OBC-43S he haʻahaʻa haʻahaʻa haʻahaʻa haʻahaʻa viscosity, hiki ke hoʻoikaika pono i ka hoʻokuʻu ʻana o ka ʻōnaehana slurry sima, ʻoiai e mālama ana i ka wai o ka slurry, pale i ka sedimentation, a me ka loaʻa ʻana o ke kūpaʻa kinoea maikaʻi.ʻOi aku ka haʻahaʻa o ka viscosity o ka shear rate haʻahaʻa ma mua o OBC-33S.
ʻO ka OBC-43S ka laulā noi nui, ke kūpaʻa wela kiʻekiʻe a hiki i ka 230 ℃, ka wai maikaʻi a me ka paʻa o ka ʻōnaehana slurry sima, ka liʻiliʻi o ka wai manuahi, ʻaʻohe lohi, a me ka hoʻomohala wikiwiki ʻana o ka ikaika mua i ka haʻahaʻa haʻahaʻa.
He kūpono ʻo OBC-43S no ka hui ʻana o ka slurry wai hou / wai paʻakai.
ʻikepili ʻenehana
'ikamu | kuhikuhi |
Ka nana aku | Pauda keʻokeʻo |
ʻO ka hana slurry sima
'ikamu | Helu kuhikuhi | Kūlana hoʻāʻo |
Pohō wai,mL | ≤100 | 80 ℃,6.9MPa |
Ka manawa mānoanoa, min | ≥60 | 80 ℃, 45MPa/45min |
Kūlike mua,Bc | ≤30 | |
Ka ikaika compressive, MPa | ≥14 | 80 ℃, kaomi maʻamau, 24h |
Wai manuahi, mL | ≤1.0 | 80 ℃, kaomi maʻamau |
ʻO ka hoʻokumu ʻana o ka slurry sima: 100% G grade sima (kiʻekiʻe sulfur kū'ē) + 44.0% wai hou + 0.6% OBC-43S + 0.5% defoamer. |
Laulā hoʻohana
Mahana: ≤230°C (BHCT).
Manaʻo manaʻo: 0.6% -3.0% (BWOC).
Pūʻolo
Hoʻopili ʻia ʻo OBC-43S i loko o kahi ʻeke hui 20kg ʻekolu-i-hoʻokahi, a i ʻole i hoʻopaʻa ʻia e like me nā koi o ka mea kūʻai aku.
ʻŌlelo
Hiki i ka OBC-43S ke hāʻawi i nā huahana wai OBC-43L.